MS-VLT120 High-Vacuum And Low-Temperature Friction Wear Tester

MS-VLT120 High-Vacuum And Low-Temperature Friction Wear Tester can be used for the evaluation of the low temperature friction and wear performance of various materials and films under vaccum and different special gas ambient.

（Test curve）

This tester uses the ball-on-disk friction principle, the technology of program temperature control system and Vacuum pumping system technology.At the same time, the sample is fixed on the test platform under the low temperature environment and rotates at a certain speed to make the surface of the ball friction coating.The friction coefficient curve and temperature setting curve can be obtained by calculating the friction signal obtained from the sensor, amplified and processed by the input computer through A / D conversion.

μ=F/N

μ—friction coefficient
F—friction force
N—normal load

Through the change of friction coefficient curve and temperature setting curve, the friction performance and wear resistance of materials or thin molds in vacuum or special atmosphere at low temperature are obtained. under a specific load, after a certain time (certain distance), the friction coefficient will be changed, in that moment, the film is worn out and the wear volume will be obtained by the weighing method. 

Key technical parameters

1. Instrument weight：80kg

2. Appearance size:600×350×550(mm×mm×mm) 

3.  Power：4.5kw

4. Operating Voltage：220V

5.Ultimate vacuum: 1×10^-3Pa

6. Vacuum pumping mode: direct molecular pump

7. Rated temperature: -120℃～room temperature 

8. Test temperature: -110℃～room temperature , multi-step heating stage

9. Heating rate: <10℃/min

10. Load:100～2000g, weight loading

11. Friction measurement range:0~10N

12.Friction Measurement accuracy: 0.1% F.S

13.Friction coefficient accuracy: < 0.01

14.Stage rotation speed: 1～1000 r/min, resolution±1 r/min

15.Sample size: Φ52mm，The thickness is 1～7mm

16.Rotation radius: 3～15 mm 

17.Mating materials diameter: Φ4 mm, Φ6 mm

18.Friction pair materials: GCr15 steel ball, AlO ceramic ball, ZrO ceramic ball, SiN ceramic ball

19.Data processing: the Access, Excel database file, Word experiment report and Jpeg picture can be generated