MRT-HT1000 Reciprocating/Rotary High Temperature Tribometer uses ball on disk settings to realize the friction performance evaluation of materials for engines, turbines ,internal combustion engines,generator components , ceramics, metal alloys, etc. at 900℃. Quantitative evaluation of wear resistance.The tester is can be also made equipped with reciprocating module, rotating module and a furnace for heating.

Key technical parameters

1.Instrument weight：80kg

2.Appearance size:530×400×700(mm×mm×mm)  

3.Loading way:

   Weight loading

   Automatic loading: constant loading、Alternating loading

4.Loading:

Weight loading:100~2000g

Automatically loading:0~50N  

5.Friction measurement range:0~50N

6.Test temperature:room temperature ～ 900℃  Multi-stage program setting

7.Heating rate: < 10 ℃/min 

8.Power：4.5kw

9.Operating Voltage：220V

10.Mating materials diameter: Φ4mm、Φ6mm

11.Friction pair materials: GCr15 steel ball, AlO ceramic ball, ZrO ceramic ball, SiN ceramic ball

12.Data processing: the Access, Excel database file, Word experiment report and Jpeg picture can be generated

9. Reciprocating module

(1) Reciprocating distance:2～40mm（The greater the stroke, the lower the frequency）

(2) Reciprocating frequency:0.05～10Hz

(3) Sample size:30×（10～55）×（1～7）（mm×mm×mm）

      The tooling shall be customized separately for other dimensions of the sample

10.  Rotation module

(1) Rotation radius:3～13mm

(2) Stage rotation speed:10～1000 r/min

(3) Sample size:Φ53mm  thickness is 1～7mm

     The tooling shall be customized separately for other dimensions of the sample